| Country | Product | Thickness (mm) | Width (mm) | Length (m) | Steel Grade | Chemical Composition | Mechanical Properties | Standard | Notes |
| Iran | Steel Sheet | 1.5 | 1000–4000 | 6–12 | ST37/ST52/S235 | Varies by grade; ST37 composition typical: C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75% | Depends on grade: yield 235–355 MPa, tensile 360–630 MPa | ISIRI 3694 / EN 10025 | Hot-rolled plate |
| Iran | Steel Sheet | 2 | 1000–4000 | 6–12 | ST37/ST52/S235 | Varies by grade; ST37 composition typical: C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75% | Depends on grade: yield 235–355 MPa, tensile 360–630 MPa | ISIRI 3694 / EN 10025 | Hot-rolled plate |
| Iran | Steel Sheet | 5 | 1000–4000 | 6–12 | ST37/ST52/S235 | Varies by grade; ST37 composition typical: C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75% | Depends on grade: yield 235–355 MPa, tensile 360–630 MPa | ISIRI 3694 / EN 10025 | Hot-rolled plate |
| Iran | Steel Sheet | 10 | 1000–4000 | 6–12 | ST37/ST52/S235 | Varies by grade; ST37 composition typical: C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75% | Depends on grade: yield 235–355 MPa, tensile 360–630 MPa | ISIRI 3694 / EN 10025 | Hot-rolled plate |
| Iran | Steel Sheet | 20 | 1000–4000 | 6–12 | ST37/ST52/S235 | Varies by grade; ST37 composition typical: C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75% | Depends on grade: yield 235–355 MPa, tensile 360–630 MPa | ISIRI 3694 / EN 10025 | Hot-rolled plate |
| Iran | Steel Sheet | 40 | 1000–4000 | 6–12 | ST37/ST52/S235 | Varies by grade; ST37 composition typical: C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75% | Depends on grade: yield 235–355 MPa, tensile 360–630 MPa | ISIRI 3694 / EN 10025 | Hot-rolled plate |
| Iran | Steel Sheet | 60 | 1000–4000 | 6–12 | ST37/ST52/S235 | Varies by grade; ST37 composition typical: C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75% | Depends on grade: yield 235–355 MPa, tensile 360–630 MPa | ISIRI 3694 / EN 10025 | Hot-rolled plate |
| Iran | Steel Sheet | 80 | 1000–4000 | 6–12 | ST37/ST52/S235 | Varies by grade; ST37 composition typical: C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75% | Depends on grade: yield 235–355 MPa, tensile 360–630 MPa | ISIRI 3694 / EN 10025 | Hot-rolled plate |
| Iran | Steel Sheet | 100 | 1000–4000 | 6–12 | ST37/ST52/S235 | Varies by grade; ST37 composition typical: C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75% | Depends on grade: yield 235–355 MPa, tensile 360–630 MPa | ISIRI 3694 / EN 10025 | Hot-rolled plate |
| Russia | Steel Sheet | 0.5 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |
| Russia | Steel Sheet | 1 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |
| Russia | Steel Sheet | 2 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |
| Russia | Steel Sheet | 5 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |
| Russia | Steel Sheet | 10 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |
| Russia | Steel Sheet | 20 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |
| Russia | Steel Sheet | 40 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |
| Russia | Steel Sheet | 80 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |
| Russia | Steel Sheet | 100 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |
| Russia | Steel Sheet | 160 | ≥500 | — | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 19903-2015 | Hot-rolled plate; coil thickness 1.2–25 mm |