| Country | Product | Leg1 (mm) | Leg2 (mm) | Thickness (mm) | Length (m) | Steel Grade | Chemical Composition | Mechanical Properties | Standard | Notes |
| Iran | L-bar (Angle) | 25 | 25 | 3 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 25 | 25 | 4 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 25 | 25 | 5 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 25 | 25 | 6 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 25 | 25 | 8 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 25 | 25 | 10 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 25 | 25 | 12 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 30 | 30 | 3 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 30 | 30 | 4 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 30 | 30 | 5 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 30 | 30 | 6 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 30 | 30 | 8 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 30 | 30 | 10 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 30 | 30 | 12 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 40 | 40 | 3 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 40 | 40 | 4 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 40 | 40 | 5 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 40 | 40 | 6 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 40 | 40 | 8 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 40 | 40 | 10 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 40 | 40 | 12 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 50 | 50 | 3 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 50 | 50 | 4 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 50 | 50 | 5 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 50 | 50 | 6 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 50 | 50 | 8 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 50 | 50 | 10 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 50 | 50 | 12 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 60 | 60 | 3 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 60 | 60 | 4 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 60 | 60 | 5 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 60 | 60 | 6 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 60 | 60 | 8 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 60 | 60 | 10 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 60 | 60 | 12 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 80 | 80 | 3 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 80 | 80 | 4 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 80 | 80 | 5 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 80 | 80 | 6 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 80 | 80 | 8 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 80 | 80 | 10 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 80 | 80 | 12 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 100 | 100 | 3 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 100 | 100 | 4 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 100 | 100 | 5 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 100 | 100 | 6 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 100 | 100 | 8 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 100 | 100 | 10 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 100 | 100 | 12 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 120 | 120 | 3 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 120 | 120 | 4 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 120 | 120 | 5 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 120 | 120 | 6 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 120 | 120 | 8 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 120 | 120 | 10 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Iran | L-bar (Angle) | 120 | 120 | 12 | 6 | ST37 | C≤0.20%, Si 0.15–0.35%, Mn 0.35–0.75%, P≤0.05%, S≤0.05% | Yield ≈235 MPa, Tensile 360–460 MPa, Elongation 25% | — | Equal angle |
| Russia | L-bar (Angle) | 25 | 25 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 25 | 25 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 25 | 25 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 25 | 25 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 25 | 25 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 25 | 25 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 25 | 25 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 30 | 30 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 30 | 30 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 30 | 30 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 30 | 30 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 30 | 30 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 30 | 30 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 30 | 30 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 40 | 40 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 40 | 40 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 40 | 40 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 40 | 40 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 40 | 40 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 40 | 40 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 40 | 40 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 50 | 50 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 50 | 50 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 50 | 50 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 50 | 50 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 50 | 50 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 50 | 50 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 50 | 50 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 60 | 60 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 60 | 60 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 60 | 60 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 60 | 60 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 60 | 60 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 60 | 60 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 60 | 60 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 70 | 70 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 70 | 70 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 70 | 70 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 70 | 70 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 70 | 70 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 70 | 70 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 70 | 70 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 80 | 80 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 80 | 80 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 80 | 80 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 80 | 80 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 80 | 80 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 80 | 80 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 80 | 80 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 90 | 90 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 90 | 90 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 90 | 90 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 90 | 90 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 90 | 90 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 90 | 90 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 90 | 90 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 100 | 100 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 100 | 100 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 100 | 100 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 100 | 100 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 100 | 100 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 100 | 100 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 100 | 100 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 120 | 120 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 120 | 120 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 120 | 120 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 120 | 120 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 120 | 120 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 120 | 120 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 120 | 120 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 150 | 150 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 150 | 150 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 150 | 150 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 150 | 150 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 150 | 150 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 150 | 150 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 150 | 150 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 200 | 200 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 200 | 200 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 200 | 200 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 200 | 200 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 200 | 200 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 200 | 200 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 200 | 200 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 250 | 250 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 250 | 250 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 250 | 250 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 250 | 250 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 250 | 250 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 250 | 250 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 250 | 250 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8509-93 | Equal angle |
| Russia | L-bar (Angle) | 63 | 40 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 63 | 40 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 63 | 40 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 63 | 40 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 63 | 40 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 63 | 40 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 63 | 40 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 75 | 50 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 75 | 50 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 75 | 50 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 75 | 50 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 75 | 50 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 75 | 50 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 75 | 50 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 90 | 56 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 90 | 56 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 90 | 56 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 90 | 56 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 90 | 56 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 90 | 56 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 90 | 56 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 100 | 63 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 100 | 63 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 100 | 63 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 100 | 63 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 100 | 63 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 100 | 63 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 100 | 63 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 125 | 80 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 125 | 80 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 125 | 80 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 125 | 80 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 125 | 80 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 125 | 80 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 125 | 80 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 150 | 90 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 150 | 90 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 150 | 90 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 150 | 90 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 150 | 90 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 150 | 90 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 150 | 90 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 175 | 100 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 175 | 100 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 175 | 100 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 175 | 100 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 175 | 100 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 175 | 100 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 175 | 100 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 200 | 125 | 3 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 200 | 125 | 4 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 200 | 125 | 5 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 200 | 125 | 6 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 200 | 125 | 8 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 200 | 125 | 10 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |
| Russia | L-bar (Angle) | 200 | 125 | 12 | 6–12.5 | St3 | C 0.14–0.22%, Si 0.15–0.30%, Mn 0.40–0.65%, P≤0.04%, S≤0.05% | Yield 225–245 MPa, Tensile 370–480 MPa, Elongation 23–26% | GOST 8510-86 | Unequal angle |